Heat Shrink Terminal made of Brass , Polyolefin and hot melt adhesive , it has good insulation, waterproof and corrosion resistance . Compared with conventional terminals , it has the advantages of durability, easy installation and low installation cost .
Shrink Ratio : 3:1
Operating temperature : -55~125℃
Initial shrinkage temperature : 80℃
Minimum complete shrinkage temperature : 130℃
Test Item | Data | Test condition | |
Unaged | tensile strength | ≧16Mpa | indoor temperature |
elongation | ≧200% | ||
Aging | tensile strength | ≧11.5Mpa | 158℃/7 days |
elongation | ≧100% | ||
Voltage resistance （Unaged） | 2.5KV，60S，No breakdown | Indoor temperature | |
Voltage resistance （Aging） | 2.5KV , 60S， Half of Unaged Voltage | 158℃/7 days | |
copper corrosion | No corrosion | 158℃/7 days | |
Copper stable | No degradation elongation≧ 100% | 158℃/7 days | |
Cold bending | No crack | -30℃/4Hours | |
Maximum secant modulus(2%) | 250Mpa | - | |
mass resistivity | ≧1014Ω-cm | - | |
thermal shock | No crack | 250℃/4hours | |