Product Description

Reinforcing Heat Shrinkable Cable Repair Sleeve

Reinforcing-Heat-Shrinkable-Cable-Repair-Sleeve

Model: HSRS-R

Descriptions:

Reinforcing Heat Shrinkable Cable Repair Sleeve HSRS-R is made from cross-linked polyolefin, with a hot-melt adhesive liner on the inner side of the sleeve. When heating, the sleeve shrinks and the adhesive melts create a water-tight bond between the sleeve and the cable. Sleeve materials equals to the material properties of the original cable jacket, it closes easily with a flexible stainless steel channel.

Features

>Quick and easy installation
>Covered with thermo paint
>Protection against mechanical stress
>Sleeve and channel can be cut to suit shorter applications
>For insulation on low voltage cable up to 1000V
>Hot melt adhesive forms a durable, moisture resistant seal
>Fit a wide range of cable sizes

Specifictions:

Size Max Cable Dia Min cable Dia Supplied Lengths Remark
HSRS-R-43/8

43

8

500,1000,1500, 2000

Other lengths are available upon requests

HSRS- R-55/12

55

12

500,1000,1500, 2000

HSRS- R-75/15

75

15

500,1000,1500, 2000

HSRS- R-100/25

100

25

500,1000,1500, 2000

HSRS- R-125/30

125

30

500,1000,1500, 2000

HSRS- R-164/42

164

42

500,1000,1500, 2000

*Alternative for Raychem CWST

Technical Data

Materials
Item Test Condition and method Requirement
Bursting Strength Test Temp:23±5°C Min 2500N
Thermal AgeingBursting Strength 168Hrs at 150±2°C (After free shrinkage)  Min 2700N 
Dielectric strength Electrode Surface Dia: 6mm Wight: 50±2gms Voltage steps:2KV/20sec Min 12 KV/mm 
Split Resistance Temp: 200±2°C                    Test time 23±3°C No splitPropagation
Carbon ContentUV Res of Out/layer Heating rate:20°C /min           Gas flow rate:300cc/min Min 2.5% 
Cold Crack Resistance Test temp≤-40°C No crack
Resistance to aggressive mediaBursting Strength Test media: Fuel oil, petroleum jelly Test temp: 70±2°C Min 2000N 
EnvironmentalStress cracking

 

10% Igepal Co 630 solution immersion Time 30 days Test Temp: 50±3°C No cracking 
Temp. indicatingpaint conversion Scraped off paint from sleeve 230-250°C
Hot melt adhesive
Item Test Condition and method Requirement
Peel Strength -PE at 23±2°C Min 100N/25mm 
Shear Strength At 23±2°C Min200N
Corrosive Effect Copper Mirror test Test time:16hrs Test temp:60±2°C No effect